The corrosion behavior of commercial aluminum in HCl was investigated by gravimetric method in absence and presence of date palm leaf extract (DPLE) as inhibitor. Corrosion rates in absence of extract ranged from 2.4-8.0 mg/cm2/h in the temperature range 20-50ºC but decreased down to 0.30-2.6 mg/cm2/h in presence of the inhibitor. Hot-water extract of date palm leaves has shown inhibition efficiency (IE) of 40- 88%at the tested conditions. IE was found to increase with increasing inhibitor concentration from 0.2 to 0.6 g/L and decrease as temperature increased. Data showed that Langmuir adsorption isotherm represents surface coverage versus extract concentration data indicating that inhibition is due to monolayer adsorption of extract components on aluminum surface. Low activation energy and enthalpy values support physical adsorption mechanism. SEM-EDS microanalysis of aluminum surface supported the inhibitive effect of the extract at the metal surface.https://www.researchgate.net/publication/272487314_Thermodynamics_and_Kinetics_of_Inhibition_of_Aluminum_in_Hydrochloric_Acid_by_Date_Palm_Leaf_Extract
The corrosion behavior of commercial aluminum in HCl was investigated by gravimetric method in absence and presence of date palm leaf extract (DPLE) as inhibitor. Corrosion rates in absence of extract ranged from 2.4-8.0 mg/cm2/h in the temperature range 20-50ºC but decreased down to 0.30-2.6 mg/cm2/h in presence of the inhibitor. Hot-water extract of date palm leaves has shown inhibition efficiency (IE) of 40- 88%at the tested conditions. IE was found to increase with increasing inhibitor concentration from 0.2 to 0.6 g/L and decrease as temperature increased. Data showed that Langmuir adsorption isotherm represents surface coverage versus extract concentration data indicating that inhibition is due to monolayer adsorption of extract components on aluminum surface. Low activation energy and enthalpy values support physical adsorption mechanism. SEM-EDS microanalysis of aluminum surface supported the inhibitive effect of the extract at the metal surface.
https://www.researchgate.net/publication/272487314_Thermodynamics_and_Kinetics_of_Inhibition_of_Aluminum_in_Hydrochloric_Acid_by_Date_Palm_Leaf_Extract
17.Apr.2024
16.Jan.2024
20.Sep.2023
أنا طالبة في الهندسة الصناعية, اختياري لهذا التخصص كان بناءً على أهميته الكبيرة كمهنة في الحاضر والمستقبل ... رغد بركات
الهندسة الصناعية تساعدك على اتخاذ قرارات أفضل، وتعطي أشكالا أخرى من مبادئ الهندسة بشكل عملي وعلمي في آن. ... محمود صلاح
قسم الهندسة الكيميائية قسم جميل جدا تعلمت فيه الكثير ومما تعلمته فيه جدية العمل وروح الفريق الواحد .. ... رغد الشويكي